ronny Posted July 4, 2009 Report Posted July 4, 2009 Hi, Can numetal be used as filler to smooth out welds or inperfections on heads or extractors. Will it be affected by high temperatures or any type of coating system such as ceramic. Thanks Quote
KBS Coatings Posted July 6, 2009 Report Posted July 6, 2009 What is the maximum temperature that you need the NuMetal to withstand? Quote
ronny Posted July 12, 2009 Author Report Posted July 12, 2009 Hi, Sorry for the delay. The max temp would be 700deg/c. If it was possible, once the filler was cured would it be able to withstand sandblasting process. Thanks. Quote
KBS Coatings Posted July 13, 2009 Report Posted July 13, 2009 NuMetal will withstands temps up to 300°F (150°C). It does not appear that NuMetal would work for your High Temperature application. Quote